Study of hydrogen separation from carbon monoxide using polyimide membrane
Publish place: 5th International Congress on Chemical Engineering
Publish Year: 1386
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,343
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC05_024
تاریخ نمایه سازی: 7 بهمن 1386
Abstract:
In this work separation of hydrogen from carbon monoxide (syngas ratio adjustment) using a hollow fiber polyimide membrane was investigated. Pure and mixed gas tests were carried out at different feed conditions. Feed pressure, temperature and flow rate was changed between 5-9 bar, 20-80 C ° and 150-300 ml/min, respectively. Membrane performance (for both gases) was obtained as a function of these parameters. Membrane permeance for hydrogen and carbon monoxide at different test conditions was between 70-130 GPU and 2.5-5 GPU, respectively.
Keywords:
Authors
Pir
Research lab for separation processes, Chemical engineering department, Iran University of Science and Technology, Narmak, Tehran, Iran
Mohammadi
Research lab for separation processes, Chemical engineering department, Iran University of Science and Technology, Narmak, Tehran, Iran
Mahdyarfar
Gas division, Research Institute of Petroleum Industry, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :