Preparation of polystyrene nanofiber modified with Dithizone using electrospinning technique

Publish Year: 1394
Type: Journal paper
Language: English
View: 468

This Paper With 7 Page And PDF Format Ready To Download

Export:

Link to this Paper:

Document National Code:

JR_SJPAS-4-7_001

Index date: 24 May 2016

Preparation of polystyrene nanofiber modified with Dithizone using electrospinning technique abstract

In this paper, polystyrene nanofiber were made using electrospinning polystyrene inside THF/DMF solvent. The major parameters such as voltage, distance between injection and collector, polystyrene concentration and rotating speed of collector were optimized in electrospinning technique. The results indicated that in specific range, with increasing voltage, high electrospinning distance, low flow of injection and high collector’s speed, we could achieve to nanofiber having regular chain structure and less diameter. In optimal condition and unmodified surface, polystyrene fiber had average diameter of 82.1 nm. Finally polystyrene absorbent by dithizone were modified and through selecting best condition, the modified polystyrene nanofiber with 92.98 nm average diameter were obtained which although it has more diameter than unmodified nanofiber, it possesses properties which the unmodified nanofiber does not have those properties, for example property of absorbing metals.

Preparation of polystyrene nanofiber modified with Dithizone using electrospinning technique Keywords:

Preparation of polystyrene nanofiber modified with Dithizone using electrospinning technique authors

D Kaviani

Department of chemistry, Science and research branch, Islamic Azad University, Tehran, Iran

M Saghi

Department of chemistry, Arak branch, Islamic Azad University, Arak, Iran

M Hajipoor

Department of chemistry, Quchan branch, Islamic Azad University, Quchan, Iran

B Assadi

Department of chemistry, Arak branch, Islamic Azad University, Arak, Iran