FORMATION OF TTANAHYDROXYAPATTENANO-BOCERAMC COATINGS VIA MAO TO IMPROVE BIOACTIVITY OF T-BASEDIMPLANTS
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 468
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_010
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
Micro Arc oxidation (MAO) was used to improve corrosion resistance and bioactivity of Ti substrates using titania-hydroxyapatite nano-bioceramic coatings. The layers were coated by applying 200, 350 and 500 V for 5, 10 and 15 min in calcium acetate and sodium phosphate containing electrolyte. Chemical composition and phase structure of coated layers were investigated using EDX and XRD analysis. The layers had comprised of different fractions of hydroxyapatite, anatase, calcium titanate and O-Tri calcium Phosphate (O-TCP) phases depend on different growing 2 S. Abbasi, F. Golestanifard and et al.conditions. Also, Crystallite size of hydroxyapatite was evaluated about 42.4 nm. SEM and AFM results indicated the preparation of porous structure with rough surface. Regarding to applied voltage and time of process, the pore size and the surface roughness of coated layers were in the range of 65-70 nm and 9.8-12.6 nm, respectively. The prepared coating under 350 V for 10 min has the maximum fraction of hydroxyapatite phase and the best CalP ratio (~1.65).
Keywords:
Authors
S. ABBASI
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, P.O Box. ۱۶۸۴۵-۱۶۱, Tehran, Iran
F. GOLESTAN-FARD
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, P.O Box. ۱۶۸۴۵-۱۶۱, Tehran, Iran
H.R REZAIE
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran
N. BARATI
School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran, Iran nastaran,