ULTRASONC-ASSISTED CO-PRECIPITATION METHOD OF PREPARATION OF NANOCOMPOSITES DIN THIE AIO,— TiO, — ZrO, SYSTEM: CHARACTERIZATION, PROPERTIESANDMICROSTURCTURE
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 296
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_049
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
Recently, the Al2O3 - TiO, -ZrO2 system has found valuable applications, particularly, as a support for NO storage-reduction (NSR) catalysts. Nanocomposite powders were prepared from the coprecipitation method in inorganic precursors under various molar ratios. The behaviors of mixed oxide nanoparticles under ultrasonic irradiation, such as dispersion, and crushing were studied. Phase transformations, crystallite size, and microstructure of the mixed oxides were investigated by STA (DTA/TG), FTIR, XRD, and SEM. XRD studies showed that zirconium titanate (ZT) is main phase, and the crystallite size varies with the final calcination temperature, and ultrasonic irradiations. SEM observations revealed that the calcination temperature strongly influences the morphology of prepared mixed oxides. The results showed that the inorganic nanoparticles in the aqueous solution can redisperse more effectively by ultrasonic irradiation than by conventional stirring. The average crystallite sizes of the nanocomposite particles heat treated at 1200°C for 2 h were in the range of 48.1-85.1 nm.
Keywords:
Authors
M. SAEIDI’’
School of Metallurgy & Materials Engineering, Iran University of Science & Technology, Tehran, Iran.
H. SARPOOLAKY
School of Metallurgy & Materials Engineering, Iran University of Science & Technology,Tehran, Iran.
S.M. MIRKAZEMI
School of Metallurgy & Materials Engineering, Iran University of Science & Technology, Tehran, Iran