PREPARATION AND CHARACTERIZATION OF DOPEDTTANA NANOPARTICILES: PREPARED) VA VATER-N-OL MCROEMULSON
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 287
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_134
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
The Microemulsion method was successfully used to prepare a series of TiO, iron oxide and SiO2 doped TiO2 nanoparticles at a doping level of 5 at. %. The molar ratio of water to surfactant Wo (= water/ Surfactant) was 2 and the samples were calcined at 350°C. The structural features of parent TiO, Fe oxide-TiO, and SiO-TiO, have been investigated by XRD, UV-Visible, SEM and TEM. The data indicated that in comparison with pure TiO2 sample, the iron oxide and SiO2 doped TiO2 samples had relatively large particle size indicating that the doping with Fe oxide and SiO2 can increase the particle size. Among all the samples, pure TiO2, Fe oxide and SiO, doped TiO, Fe oxide TiO, sample showed the highest activity on the photocatalytic decomposition of methylene blue.
Keywords:
Authors
M. KARBASSI
Science and Research Branch Islamic Azad University, P.O. Box ۱۴۱۵۵-۴۹۳۳, Ponak Ave., Tehran, Iran.
A. NEMATI
Department of Materials science and Engineering, Sharif University of Technology, P.O. Box ۱۱۱۵۵-۹۴۶۶, Azadi Ave., Tehran, Iran
M. HOSSINIE ZADI
Department of Inorganic Pigments and Glazes, Institute for Colorants, Paint and Coatings, P.O.Box ۱۶۶۸۸۱۴۸۱۱, Vafananesh Ave., Tehran, Iran