A NANO SIC-SINOXIDATION PROTECTIVE COATING PREPARED BY ELECTROPHORETC DEPOSITION AND DIRECT NITRDATION
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 450
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_153
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
In this study, EPD, as a simple and low cost method, was used to coat the graphite substrate with a nano-sized SiC-Si oxidation protective coating with the ratio of 1:1. Different organic solvents used as suspension media in pre-experiments and finally Ethanol as the media, 1.4 g L of iodine as the additive, and coating parameters of 180s and 40 V for time and voltage respectively, were applied. Analysis of the kinetics of deposition revealed a linear behavior which changed as the coating thickened. In order to increase the strength of the coating and formation of SiN, direct nitridation was performed at 1400 and 1450 °C. The latter was found to be more appropriate. Microstructural analysis and recognition of phases were performed using SEM and XRDrespectively.
Keywords:
Authors
M. SHAHIRLARI
Department of Materials Science and Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran
P. ALIZADEH
Department of Materials Science and Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran
S. A. KHALIFE SOLTANI
Department of Composites Research, Malek Ashtar University, P.O Box ۱۱۳۶۵-۹۴۶۶, Tehran, Iran
V. KHANI
Department of Materials Science and Engineering, Tarbiat Modares University, P.O. Box ۱۴۱۱۵-۱۴۳, Tehran, Iran