COMPRESSIVE AND WEAR PROPERTIES OF AL-BCNANOCOMPOSITES PREPARED VIA MECHANCAL MLLNGAND HOT EXTRUSION
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 342
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_252
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
Mechanical milling was used to synthesize Al nanostructured powder in a planetary ball-mill under argonatmosphere up to 20 h. The same process was conducted for Al-4 wt.% B4C nanocomposite powders to explore the role of nanosize reinforcements on mechanical milling stages. The results show that the addition of boron carbide particles accelerate the milling process, leading to a faster work hardening rate and fracture of aluminum matrix.Compressive and wear properties of a nanostructured matrix of Al prepared via mechanical milling and hot extrusion were investigated before and after incorporation of B4C nanoparticles. The results revealed a lower wear rate, higher compressive strength and hardness for nanostructured Al matrix in comparison with the commercial coarse grained Al matrix. The same pattern was also observed in the nanocomposite samples with respect to the base matrix.
Keywords:
Authors
A. ALIZADEH
Department of Materials Science and Engineering, Tarbiat Modares University, Tehran, P.O. Box. ۱۴۱۱۵-۱۴۳, Iran
E. TAHER-NASSAJ
Department of Materials Science and Engineering, Tarbiat Modares University, Tehran, P.O. Box. ۱۴۱۱۵-۱۴۳, Iran