Swelling behavior of Sulfonated Polyacrylamide Nanocomposite Hydrogels in Electrolyte Salt Solutions
Publish place: 06th International Congress on Chemical Engineering
Publish Year: 1388
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,661
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC06_481
تاریخ نمایه سازی: 1 مهر 1388
Abstract:
Nanocomposite hydrogels were prepared by crosslinking of aqueous solutions of sulfonated polyacrylamide / sodium montmorillonite with chromium triacetate. The effect of nanoclay content on equilibrium swelling ratio in NaCl and CaCl2 solutions, ultimate storage modulus and crosslink density were evaluated. In addition, experimental swelling results of these nanocomposite gels (NC) was compared with predictions of Flory-Rehner theory modified by Vasheghani-Farahani et al.(V-F model). The limiting storage modulus of the NC gels decreased for montmorillonite content of 1000ppm, while for montmorillonite loading greater than 1000ppm, there is an increase in the limiting storage modulus of the NC gels. The equilibrium swelling ratio of the NC networks decreased with increase of montmorillonite content in both NaCl and CaCl2 solutions. In addition, the V-F model was sensitive to clay concentration and that the swelling data for NC gels in dilute salt solutions can be well represented by V-F model. However, with increasing salt concentration, theoretical predictions show some deviations from experimental results.
Keywords:
Authors
Jamal Aalaie
Chemical Engineering Department, Tarbiat Modares University, Jalal Al Ahmad Highway, P.O. Box ۱۴۱۵۵-۱۴۳, Tehran, Iran
Ebrahim Vasheghani-Farahani
Chemical Engineering Department, Tarbiat Modares University, Jalal Al Ahmad Highway, P.O. Box ۱۴۱۵۵-۱۴۳, Tehran, Iran
Ali Rahmatpour
Polymer Science and Technology Division, Research Institute of Petroleum Industry (RIPI), P.O. Box ۱۸۷۴۵-۴۱۶۳, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :