Multi-wall carbon nanotubes formation by using Metal Dusting process
Publish place: 2nd National Nano Materials and Nano Technology Conference
Publish Year: 1389
نوع سند: مقاله کنفرانسی
زبان: English
View: 2,414
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NAYRC02_100
تاریخ نمایه سازی: 10 دی 1388
Abstract:
Laboratory tests were designed to produce accelerated metal dusting by exposing 304L austenitic stainless steel to a 50CO-50H2 (vol. pct) gas mixture at 620oC for 300 hours. Surface morphology of the samples was examined by stereoscopy and SEM with EDS attachment. The carbonaceous depositions on sample surface were analyzed using SEM and TEM. In this paper, we demonstrate that multi-wall CNTs can be prepared by exploiting the metal dusting process. It has been confirmed herein that the amount of the CNTs remarkably increases when the reaction time is extended up to 300 hours, indicating a possibility of the mass production.
Authors
h Ghorbani
Iran University of Science and Technology, Master of science student.
S Rastegari
Iran University of Science and Technology, Assistant Professor
S Mirdamadi
Iran University of Science and Technology, Professor.
A Rashidi
Research Institute of Petroleum Industry, Assistant Professor
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :