Comparison between Biaxial Flexural Strength and Microstructure of Polished and Glaze-Fired Specimens of Zirconia Lithium Silicate Glass Ceramic
Publish place: Journal of Dental Materials and Techniques، Vol: 8، Issue: 3
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 403
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-8-3_002
تاریخ نمایه سازی: 18 تیر 1398
Abstract:
Introduction: There has been a growing interest in glass ceramic systems with good esthetics, high fracture resistance, bonding durability, and simplified fabrication techniques using CAD/CAM. The aim of this study was to compare flexural strength in polished and glazed and fired specimens of zirconium lithium silicate (ZLS) CAD/CAM blocks Celtra Duo. Methods: A total of 14 specimens of Celtra Duo (Dentsply Sirona, Germany) were designated and equally divided into two groups, including group I (n=7; as polished) and group II (n=7; as glazed and fired) according to the manufacturers’ instructions. Then biaxial flexural strength was tested according to ISO 6872 using a universal testing machine and piston-on-three-ball method after polishing, glazing, and firing. The fractured surfaces and microstructure were observed by scanning electron microscope (Jeol/GSM5300). Data were then statistically analyzed using SPSS software (version 20.0). Results: There were statistically significant differences in biaxial flexural strength between a polished and glaze-fired specimen of ZLS glass ceramic discs as biaxial flexural strength was lower in polished specimens (mean±standard deviation: 158.7±21.67 MPa), while the glazed specimens showed higher biaxial flexural strength (mean±standard deviation: 261.5±31.89 MPa). Conclusion: Glazing and firing of Celtra Duo specimens increased biaxial flexural strength significantly in comparison to polishing with no significant change in the microstructure.
Keywords:
Authors
Alaa M. Attaallah
Dental Student, Faculty of Dentistry, Pharos University, Alexandria, Egypt
Eman M Zayed
Dental Student, Faculty of Dentistry, Pharos University, Alexandria, Egypt
Salma M Dabees
۱Dental Student, Faculty of Dentistry, haros University, Alexandria, Egypt
Youssef Y Ashour
Assistant Lecturer of Fixed Prosthodontics, Faculty of Dentistry, Pharos University, Alexandria, Egypt
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :