Influence of artificial aging on the shear bond strength of zirconia-composite interfaces after pretreatment with new 10-MDP adhesive systems
Publish place: Journal of Dental Materials and Techniques، Vol: 5، Issue: 1
Publish Year: 1395
نوع سند: مقاله ژورنالی
زبان: English
View: 297
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JDMT-5-1_001
تاریخ نمایه سازی: 20 مهر 1398
Abstract:
Introduction: This in-vitro study investigates the bond strength of different zirconia composites with three different modern adhesive systems after artificial aging using thermocycling and water storage. Methods: A total of 90 specimens of zirconia (InCoris, Sirona, Germany, Bernsheim) were ground using a 165 µm grit rotating diamond disc. Thirty specimens were additionally treated with either Futurabond U FBU (VOCO GmbH), or Futurabond M+ FBM (VOCO GmbH) or Futurabond M+ in combination with the DCA activator FBMD (VOCO GmbH). One of the three different types of composites – BifixSE BS , BifixQM BQ or GrandioSO G (VOCO GmbH) – was bonded to the ten specimens of each group. All of the specimens underwent artificial aging using thermocycling between 5°C and 55°C for 5000 cycles followed by water storage for 100 days. Shear bond strength (SBS) was determined in a universal testing machine. The type of failure was evaluated using fluorescence microscopy. The data were compared to existing data without artificial aging. Statistical analysis was performed with ANOVA and the Tukey test. Results: FBM and FBMD had higher SBS than FBU in combination with all tested composites, except BifixSE. In nearly all groups, artificial aging had no effect, with the exception of the combination of FBMD with BifixSE, in which there was a significant decrease in SBS after the aging process (p<0.001). Conclusion: The new 10-MDP-containing adhesive systems including FBU, FBM and FBMD are insensitive to the aging process tested in this study.
Keywords:
Authors
p.c pott
Department of Prosthetic Dentistry and Biomedical Materials Research, Hannover Medical School, Carl-Neuberg-Str. ۱, ۳۰۶۲۵ Hannover, Germany
M Stiesch
Department of Prosthetic Dentistry and Biomedical Materials Research, Hannover Medical School, Carl-Neuberg-Str. ۱, ۳۰۶۲۵ Hannover, Germany
M Eisenburger
Department of Prosthetic Dentistry and Biomedical Materials Research, Hannover Medical School, Carl-Neuberg-Str. ۱, ۳۰۶۲۵ Hannover, Germany
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :