Microstructure, mechanical and thermal properties of chalcogenide glasses and glass-ceramics based on Se-As-Ge system nucleated by Sn
Publish place: Advanced Ceramics Progress، Vol: 5، Issue: 1
Publish Year: 1398
نوع سند: مقاله ژورنالی
زبان: English
View: 424
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-5-1_003
تاریخ نمایه سازی: 23 مهر 1398
Abstract:
In particular, chalcogenide glasses and glass-ceramics are new materials that exhibit good transparency in infrared region (0.8-12µm). We can overcome the main weakness of these glasses by improving the hardness through controlling crystallization. In this paper, we report results of a study on chalcogenide glasses in the ternary system of As-Se-Ge with nominal composition of Snx (Se0.6As0.1Ge0.3)100-x (x=0, 2, 4 and 6 mol %) which is suitable for use in optical devices. Melt quench technique was used for preparing alloy specimens. Glass-ceramics were made using an appropriate heat-treatment temperature and time from Snx (Se60As10Ge30)100-x glasses in order to improve the mechanical properties. The temperature of the heat treatment started with the peak temperature (Tp) for glasses and different characteristics of prepared glasses such as glass transition temperature, hardness, density, transmittance, and microstructure were determined. Initially, Tg temperature was decreased with the addition of Sn, but with an increase of Sn up to 6 mol%, Tg was increased due to structural cohesion and formation of long chains of selenium. In this study, the highest value of the hardness for the Se60Ge30As10Sn6 glass was obtained after heat treatment and forming a crystalline phase while maintaining the initial transmittance.
Keywords:
Authors
Saideh Ahmadpour
Department of Materials Science and Engineering, University of Tabriz, Iran
Mohammad Rezvani
Department of Materials Science and Engineering, University of Tabriz, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :