Cyclic oxidation behavior of uncoated and aluminum-rich nickel aluminide coated Rene-80 superalloy
Publish place: Advanced Ceramics Progress، Vol: 4، Issue: 4
Publish Year: 1397
نوع سند: مقاله ژورنالی
زبان: English
View: 427
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ACERPT-4-4_001
تاریخ نمایه سازی: 23 مهر 1398
Abstract:
In this study, aluminide coating was employed to enhance the high-temperature cyclic oxidation of Rene-80 superalloy at 950ºC. The microstructural aspects and phase constituents of samples were investigated with scanning electron microscopy (SEM) and x-ray diffraction (XRD) techniques. The result of oxidation tests showed that the weight gain in the uncoated sample was considerably higher than the aluminide coated sample, which indicates the higher rate of oxide formation on the uncoated surface. With the aid of microstructural and XRD analysis, it was confirmed that with the increment of oxidation cycles, the thickness of aluminide coating reduced and the protective β-NiAl phase was converted to alumina scales. According to the EDS results taken from the top coat, it was found that with the increase of oxidation cycles, the content of aluminium in the top layer was drastically decreased and the weight percentage of oxygen was considerably enhanced. Also, in higher oxidation cycles, other protective elements such as Cr and Ti outwardly diffused from the inter-diffusion zone (IDZ) layer which led to reduction in the content of these elements in inner zones of the aluminide coating.
Keywords:
Authors
Mosleh Naderi
Ceramic Division, Materials and Energy Research Center, Karaj, P.O. Box ۳۱۷۸۷-۳۱۶, Iran
Mohammad Farvizi
Ceramic Division, Materials and Energy Research Center, Karaj, P.O. Box ۳۱۷۸۷-۳۱۶, Iran
Kourosh Shirvani
Department of Advanced Materials and New Energies, Iranian Research Organization for Science and Technology (IROST), Tehran ۱۵۸۱۵-۳۵۳۸, Iran
Mohammad reza Rahimipour
Ceramic Division, Materials and Energy Research Center, Karaj, P.O. Box ۳۱۷۸۷-۳۱۶, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :