Sintering of Glass - Steel Slag-SiC Composite as a Foam
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 213
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-8-3_003
تاریخ نمایه سازی: 9 مرداد 1400
Abstract:
Foam glass-ceramics are porous material with the desired strength. In this work, steel slag was mixed with soda lime glass in (۲۰, ۴۰, ۵۰, ۶۰, ۷۰ wt. %,denoted by SG۲۰,SG۴۰,SG۵۰,SG۶۰,SG۷۰) and ۵ wt.% SiC. Giving to Hot stage microscopy images, glass-slag composite's contraction starts at ۱۰۵۰ºC. According to the SEM micrographs the tunnel-like pore porosity resulted from the decomposition of carbide phase were formed. The sizes of pors varies in ۵۰۰ - ۱۰۰۰ μm range. More over by the ۵۰ wt. % soda lime glass addition and sintering at ۱۲۰۰ ° C, the spherical porosity were formed and the size of the porosity were reduced to ۵۰ μm in these composites. Also, by the the glassy phase increasing, the total porosity was increased to ۸۰%, the density decreased to ۰.۸g / cm۳in SG۴۰. This composite as a porous material has ۲ to ۵ MPa bending strengths. Wollastonite phase was detected in these composite.
Authors
aida faeghinia
Department of Ceramic, Materials and Energy Research Center, Meshkindasht, Alborz, Iran
hossein mardi
Department of Ceramic, Materials and Energy Research Center, Meshkindasht, Alborz, Iran
soosan hasheminia
Department of Engineering, Marand Branch, Islamic Azad University, Mrand, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :