Evaluation of the Combined Use of Waste Paper Sludge Ash and Nanomaterials on Mechanical Properties and Durability of High Strength Concretes
Publish Year: 1400
نوع سند: مقاله ژورنالی
زبان: English
View: 280
This Paper With 14 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-34-7_010
تاریخ نمایه سازی: 12 مرداد 1400
Abstract:
The paper industry burns or buries a significant amount of waste paper sludge. This issue is not suitable from environmental and economic aspects. In this study, the mechanical and durability properties of high-strength concrete containing waste paper sludge ash (WPSA) were evaluated. The variables were WPSA (۰, ۵, ۱۰, and ۱۵% by weight of cement), silica nanoparticles (۰ and ۲.۵ by weight of cement), and aluminum oxide nanoparticles (۰ and ۲.۵ by weight of cement). Compressive strength, splitting tensile strength, flexural strength, and ultrasonic pulse velocity testswere conducted to evaluate the mechanical properties. The durability properties were also investigated using water penetration depth, water absorption, and electrical resistivity tests. The microstructure of the specimens was analyzed by preparing electron microscopic images. The combined effect of WPSA and nanoparticles on improving the mechanical and durability properties of high-strength concrete are better than using each of them alone. WPSA and nanoparticles react with calcium hydroxide formed due to cement's hydration, and silica produces hydrated calcium, which is the hard material that makes concrete strength. Consumption of calcium hydroxide and production of more hydrated calcium silicate in the presence of nanoparticles and WPSA are among the reasons for water absorption reduction, increased electrical resistance, and water penetration depth reduction in concrete specimens. By replacing part of the cement with WPSA, silica nanoparticles, and aluminum oxide nanoparticles, the transition zone between the aggregates strengthens, and the tensile and flexural strengths increased
Keywords:
Waste paper sludge ash , Aluminum Oxide Nanoparticles , Silica Nanoparticles , Durability properties , Mechanical properties , high strength concrete
Authors
F. Delaram
Department of Civil Engineering, Qeshm Branch, Islamic Azad University, Qeshm, Iran.
Y. Mohammadi
Department of Civil Engineering, University of Mohaghegh Ardabili, Ardabil, Iran.
M.R. Adlparvar
Department of Civil Engineering, University of Qom, Qom, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :