Reinforcement of Glass Ionomer Cement: Incorporating with Silk Fiber
Publish Year: 1395
نوع سند: مقاله ژورنالی
زبان: English
View: 154
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-4-3_002
تاریخ نمایه سازی: 12 مهر 1400
Abstract:
The aim of this study was to synthesis of glass ionomer-silk fiber composite and to evaluate the effect of adding natural degummed silk fiber on the mechanical properties of glass ionomer cement (GIC). For this purpose, natural degummed silk fibers with ۱ mm in length and ۱۳-۱۶ µm in diameter were added to the ceramic component of a commercial glass ionomer cement in ۱, ۳ and ۵ wt. %. Compressive strength (CS), three-point flexural strength (FS) and diametral tensile strength (DTS) of the prepared glass ionomer-silk fiber were measured. Analysis of variance (ANOVA) was used to compare the obtained results. Moreover, SEM technique was used for investigation of the surface morphology of as-prepared composite and fractured area. The results showed that the highest compressive strength, flexural strength and diametral tensile strength were obtained using ۳, ۳ and ۵ wt. % of silk fiber, respectively. However, at ۳ wt. % silk fiber, all three measures of strength exhibited a significant increase compared to the commercial GIC. Therefore, it can be suggested that the addition of ۳ wt. % silk fiber to the ceramic component of GIC is desired for dental restorations and orthopedic implant applications, where the maximum strength in all three modes of loading would be beneficial.
Keywords:
Authors
Mina Bahrami-Abadi
Young Researchers and Elite Club, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
Masoumeh Khaghani
Young Researchers and Elite Club, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
Ahmad Monshi
Advanced Materials Research Center, Faculty of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Ali Doostmohammadi
Materials Department, Engineering faculty, Shahrekord University, Shahrekord, Iran.
Sara Alizadeh
Young Researchers and Elite Club, Najafabad Branch, Islamic Azad University, Najafabad, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :