Crack Behavior of the Aluminum Alloy ۲۰۲۴ Under Fretting Conditions
Publish Year: 1381
نوع سند: مقاله ژورنالی
زبان: English
View: 148
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-15-3_007
تاریخ نمایه سازی: 19 اسفند 1400
Abstract:
The initial stage of fretting fatigue crack growth is significantly influenced by tangential force induced by fretting action along the contact surface where a mixed-mode crack growth is involved. Fretting crack behavior of aluminum alloy ۲۰۲۴ was studied, taking into account the problem of contact asperities. Finite element was used for the determination of the stress field near the contact surface and the stress intensity factor. The results showed that tensile stress maxima are situated at the trailing edge of the contact zone. Experimental results showed that the crack initiates from the trailing edge of the contact zone too. The crack extension angle was calculated and compared with experimental results at different normal loads. The stress intensity factor increased with increasing friction. The crack initially grows in combined mode I and II before deflecting to mode I plane. Delamination, one of the wear mechanisms, has been observed in our experiments too.
Keywords:
Authors
G. H. Majzoobi
Engineering, Buali Sina University
G. H. Farrahi
School of Mechanical Engineering, Sharif University of Technology