Preparation of Porous Alumina/Nano-Nickel Composite by Gel Casting and Carbothermic Reduction

Gel casting, carbothermic reduction, and sintering were used to make a porous alumina-based body containing nickel nano-particles. Effects of dispersant (Tri polyphosphate sodium) amount on gel viscosity, mechanical activation of raw materials, raw materials mixture composition, and reduction atmosphere on the prepared composites and NiO reduction mechanism were investigated. XRD, SEM, and TG-DTA analyses were used to characterize the resulting products. It was found that ۲.۵ wt % dispersant is an optimum amount for a gel suspension with ۵۰ V% of solid consisting of alumina, graphite, and nickel oxide. XRD results of reduced and sintered product (at ۱۲۰۰-۱۵۰۰ °C) showed that alumina, nickel, and nickel aluminate spinel are present in the prepared composite. SEM images of the composite showed that nickel nanoparticles and porosities with different dimensions are present in the alumina body. The porosity of the composite made with ۱۲ h ball milled-alumina was ۴۸%, while it was ۶۴ % in the sample made with ۲۰ min ball-milled alumina. The results of TG-DTA analyses showed that the reduction temperature and mechanism are dependent on the raw materials’ ball milling time. Thermal analyses revealed that mechanical activation of raw materials decreases the NiO reduction temperature and increases the metallic Ni production.

Keywords:

Alumina , nickel , Composite , gel casting , reduction , porosity