Synthesis and characterization of poly vinyl alcohol/poly vinyl pyrrolidone/MnTiO3 nano-hybrids for PEM fuel cells
Publish place: Second National Conference on Hydrogen and Fuel Cells
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 2,843
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
H2FC02_053
تاریخ نمایه سازی: 27 شهریور 1391
Abstract:
PVA (poly vinyl alcohol)-MnTiO3 (PM) and PVA-PVP (poly vinyl pyrrolidone)-MnTiO3 (PPM) nanocomposite membranes have been prepared with solutions casting method. Glutaraldehyde (GA) was used as cross linking agent. The results showed that the proton conductivity and water uptake of the nanocomposite membranes due to hydrophilic nature of MnTiO3 nanoparticles were higher than that of the PVA membrane. PPM membranes containing 5 wt. % of MnTiO3 nanoparticles and PVA:PVP 80:20, demonstrated higher thermal stability, water uptake (3107) and proton conductivity (2.1 ×10-2 S/cm) than PM membranes, due to hydrophilic effect of PVP, which can made strong hydrogen-bonding, intense intra-molecular interaction and reduce the crystallinity of the PVA polymer.
Keywords:
Authors
Khadijeh Houshyari
Department of Chemistry, Amirkabir University of Technology, Tehran, I.R.Iran,
Mehran Javanbakht
Department of Chemistry, Amirkabir University of Technology, Tehran, I.R.Iran,
Leila Naji
Department of Chemistry, Amirkabir University of Technology, Tehran, I.R.Iran,
Morteza Enhessari
Department of Chemistry, Islamic Azad University, Naragh Branch, Naragh
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :