Investigating Tribological Characteristics of Ni-P and Double–Layered Ni-P/Ni-B Electroless Coatings Applied to the Carbon Mild Steel Ck۴۵
Publish Year: 1391
نوع سند: مقاله ژورنالی
زبان: English
View: 50
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-9-2_001
تاریخ نمایه سازی: 6 آبان 1402
Abstract:
In this research, tribological characteristics of Ni-P electroless coating and double-layered Ni-P/Ni-B electroless coating were studied. For this purpose, Ni-P electroless coating with ۲۵ μm thickness was initially applied to the surface of steel Ck۴۵ samples; then, a double-layered Ni-P/Ni-B electroless coating, including inner layer of Ni-P with ۱۵ μm thickness and outer layer of Ni-B with ۱۰ μm thickness, was applied to the surface of similar samples and were heat treated at ۴۰۰˚C for ۱ h. Effect of heat treatment on morphology, structural variations and wear behavior of coating was investigated using different tests such SEM, XRD and pin on disk wear test at room temperature. Hardness of the obtained coatings was measured by a Vickers microhardness machine prior and after heat treatment of the samples. The results showed that the double-layer coating with the same thickness in each layer improved hardness and wear resistance compared to the single-layer coating. Heat treatment led also to the creation of nano crystalline structure; therefore, hardness and wear resistance of the coating increased due to change in structure from amorphous to crystalline structure and created rigid phases of Ni۳P.
Keywords:
Authors
A. Baibordi
Department of Materials Engineering, Shiraz University, Shiraz, Iran
M. Bina
Department of Advanced Materials and Renewable Energy, Iranian Research Organization for Science and Technology, Tehran, Iran
K. Amini
Department of Engineering, Tiran Branch, Islamic Azad University, Tiran, Iran
A. Dehghan
Department of Materials Engineering, Shiraz University, Shiraz, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :