Investigation on Effect of Pulse Cathodic Protection on CP Penetration Depth Under the Tape Coating Disbondment on Pipeline Steel
Publish Year: 1399
نوع سند: مقاله ژورنالی
زبان: English
View: 63
This Paper With 14 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ICAC-9-37_002
تاریخ نمایه سازی: 5 آذر 1402
Abstract:
The effect of pulse cathodic protection (CP) on CP penetration depth under tape coating disbondment of pipeline steel has been investigated in this study and results have been compared with conventional CP. In this regard, a laboratory cell with the length of ۲۰۰۰ mm that can simulate the underlying conditions by applying CP was designed and made. For investigation of crevice width on CP penetration depth coupons with dimensions of ۲۰۰۰×۱۰ mm and ۲۰۰۰×۵۰ mm made from API X-۵۲ pipeline steel were placed under coating disbondment with the gap size of ۳ mm and different widths. By placing the cell in a simulated soil solution C۲, the potential of ۱۰۰۰mVSCE through two methods of conventional & pulse CP with the frequency of ۱۰۰۰۰ Hz was applied to the open mouth (OM) of the simulated coating disbondment. Result showed by applying conventional CP for both the crevice widths, potential failed sharply to Open Circuit Potential (OCP) near to the OM while for pulse CP, in contrast to conventional CP, which CP penetration depth was increased. At the crevice with the width of ۵۰ mm CP level was measured more than the width of ۱۰ mm, such that the entire disbondment length was protected by CP. The lower CP level for the crevice with the width of ۱۰ mm could be due to concentration polarization resistance which restricted the penetration of the positive current within the crevice. Also, pH value under the coating disbondment with applying pulse CP at the crevice with the width of ۵۰ mm was measured more than the pH value for the disbondment with ۳۰ mm width other due to higher CP level under this disbondment. In summary, results showed despite the conventional CP, applying pulse CP with high frequency could be an effective method in increase of the CP penetration depth under tape coating disbondments.
Keywords:
Authors
عبدالمجید اسلامی
دانشگاه صنعتی اصفهان
حسین نجفی محترم
دانشگاه صنعتی اصفهان
محمدعلی گلعذار
دانشگاه صنعتی اصفهان
مهدی احمدی
شرکت گاز استان اصفهان
امین کاویان
شرکت گاز استان اصفهان