Preparation of Polyaniline-Clay Nanoadditive and Investigation on Anticorrosion Performance in Epoxy Coating
Publish Year: 1394
نوع سند: مقاله ژورنالی
زبان: English
View: 84
This Paper With 11 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JPSTR-5-2_001
تاریخ نمایه سازی: 29 آذر 1402
Abstract:
The corrosion protection of mild steel by a newly developed epoxy-based coating system containing inherently conducting nanopolyaniline-clay as a nanoadditive has been studied. Polyaniline-clay anticorrosion nanoadditive (PCNA) was obtained by the direct mixing method of nanopolyaniline (۰.۰۳ wt.%) and organo-modified clay (۳ wt.%) at atmospheric pressure, and XRD technique was used to study d-spacing of clay platelets in the prepared nanoadditive. PCNA was dispersed in polyaminoamide hardener matrix and was used for epoxy coating (EPCNA) preparation. The particle size of the polyaniline in hardener was determined using dynamic light scattering technique (DLS). The results revealed that the particles were in the range of ۵۰–۵۸ nm. The degree of exfoliation and distribution and particles size were studied by XRD and TEM in the final dried film. The corrosion protection ability of EPCNA was compared to an epoxy coating containing pure nanopolyaniline (ENPN) using electrochemical impedance spectroscopy (EIS) and salt spray methods. In addition, an investigation on the morphology of metal-coating interface by scanning electron microscopy (SEM) technique in ENPN and EPCNA samples after salt spray test showed stable oxide layer formation for ENPN and a dense stable oxide layer for EPCNA on metal surface. The results showed that the PCNA nanoadditive enhanced corrosion protection effect in comparison to pure nanopolyaniline (NPN) in the epoxy coating.
Keywords:
Authors
Mohammadreza Bagherzadeh
Nanotechnology and Carbon Research Group, Faculty of Downstream Petroleum Industry, Research Institute of Petroleum Industry (RIPI), Tehran, Iran
Mahdi Ghasemi
Coating Research Group, Industrial Protection Research Division, Research Institute of Petroleum Industry, N.I.O.C., Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :