Effect of NiO Sintering Aid on the Electrical Properties of KNN-LST Lead-free Piezoceramics
Publish place: Advanced Ceramics Progress، Vol: 10، Issue: 1
Publish Year: 1403
Type: Journal paper
Language: English
View: 36
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- I'm the author of the paper
Export:
Document National Code:
JR_ACERPT-10-1_006
Index date: 26 November 2024
Effect of NiO Sintering Aid on the Electrical Properties of KNN-LST Lead-free Piezoceramics abstract
The current research focuses on the synthesis and characterization of sodium potassium niobate (KNN), a lead-free piezoelectric compound. The objective is to replace lead-based compounds like PZT using KNN-LST, which is sodium potassium niobate piezoceramic powder doped with lithium, antimony, and tantalum. To this end, solid-state method was employed to sinter the samples at 1110 °C with varying percentages of NiO sinter aid (0%, 0.75%, 1.5%, and 2.25%). X-ray diffraction analysis confirmed the formation of pure KNN-LST perovskite phase at 1110 °C with a composition containing 1.5% NiO. Scanning electron microscope images also demonstrated that cubic particles inherent in KNN were observed in samples with no NiO addition as well as those containing 0.75% and 1.5% NiO; however, these particles were transformed into cylindrical grains when incorporating 2.25% NiO. With an increase in the sintering percentage from zero NiO content to higher amounts, sample density also increases from approximately 85% up to its peak at around 94%, followed by a slight decrease by about 91%. Similarly, the dielectric coefficient increased from approximately850 without any contribution from NiO sinter addition up to1500 upon addition of 1.5%NiO sinter but then, it decreased again by approximately 1200 followed by addition of 2.25% NiO sinter. Conversely, dielectric loss initially reduced from roughly 0.14% during no NiO sinter addition by merely 0.04% during 1.
Effect of NiO Sintering Aid on the Electrical Properties of KNN-LST Lead-free Piezoceramics Keywords:
Effect of NiO Sintering Aid on the Electrical Properties of KNN-LST Lead-free Piezoceramics authors
Mehdi Delshad Chermahini
Assistant Professor, Department of Materials Engineering, Faculty of Engineering, University of Shahrekord, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :