Synthesis of Hydroxyapatite mesoporous nanoparticles at low temperature via chemical precipitation
Publish place: دومین کنفرانس بین المللی پژوهش در علوم و تکنولوژی
Publish Year: 1394
نوع سند: مقاله کنفرانسی
زبان: English
View: 469
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CRSTCONF02_211
تاریخ نمایه سازی: 21 شهریور 1395
Abstract:
In the present study, mesoporous hydroxyapatite (HA) nanopaticles was succesfully synthesized via aqueous chemical precipitation. Sample was characterized with BET-BJH, XRD, FE-SEM. It was found that HA Nanoparticles with hexagonal structure can be synthesized at low temperatures. X-ray diffraction was approved this. FE-SEM images of HA nanoparticles showed spherical morphology with 40 nm in diameter. BET analysis approved mesoporous structure
Keywords:
Authors
Motahare Sadat Mohseni Salehi Monfared
Graduate Student at Depertment of Materials Science and Engineering,Tarbiat Modares University (TMU)
Jafar Javadpour
Professor at Faculty of Materials Science and Engineering,Iran University of Science and Technology (IUST)
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :