Vertically-aligned Mn3O4 Nanorods: Electrochemical Preparation and Characterization
Publish place: 11th Annual Electrochemistry Seminar of Iran
Publish Year: 1394
نوع سند: مقاله کنفرانسی
زبان: English
View: 277
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ELECTROCHEMISTRY011_306
تاریخ نمایه سازی: 5 بهمن 1395
Abstract:
Since manganese oxides have unique electrical and chemical properties, it can be used as an electrode material for capacitors, electrochromic devices, ion-exchangers, and selectiveadsorption material of radio nuclides. Electrochemical supercapacitors are becoming attractive energy storage devices for applications involving high power requirements. There is an increasing interest in the development of advanced electrode materials based on manganeseoxides. Nanostructured manganese oxides have been reported to show a promising as electrodes for lithium secondary batteries and supercapacitors, as well as redox catalysts. The preparation of nanowires and nanorods of metal oxides is of considerable interest. Herein, we reportelectrochemical synthesis of Mn3O4 nanorods and their supercapacitive performance. Deposition experiments were performed in manganese chloride bath and direct current mode with applying 2 mA/cm2. XRD analysis (Fig. 1a) showed that the product is crystalline Mn3O4 phase (JCPDS no.42-1124). SEM observation showed a rod texture with regular arrangement, i.e. vertically-alignarrangement. Fig. 2 shows the supercapacitive performance of the prepared Mn3O4. The specific capacitances of Mn3O4 nanorods were calculated to be 302.1, 285.8, 237.5, 202.1, 168.5 and 118 F g–1 at the scan rates of 2, 5, 10, 25, 50 and 100 mV s−1, respectively (Fig. 2b). These values showed excellent supercapacitive performance of the prepared Mn3O4 nanorods