INVESTIGATIONSON THIEAL-CURODREINFORCEDCOMPOSITE FABRCTED BY TWST EXTRUSION
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 289
This Paper With 9 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_272
تاریخ نمایه سازی: 10 تیر 1396
Abstract:
Twist Extrusion (TE) is one of SPD (Severe Plastic Deformation) method to fabricate ultrafine grain bulk materials. In this paper, Twist Extrusion was introduced to fabricate the Al-Cubar reinforced composite. The microstructural evolution and phase constitution near the joining interface of Al/Cu composites were evaluated using optical and scanning electron microscope as well as X-ray diffraction (XRD). Microhardness testing was used to evaluate the hardness of Al, Cu and the interface of composite after each passes of TE. Shear test was used to measure the bonding strength of interface in fabricated composites. Shear tests show that the strength and hardness of interface is lower than that of copper rod and higher than that of Al matrix. XRD results show that after 2 passes of deformation CuAl2 and CuAl4 intermetalics were produced at the interface of composite. Fine grains of intermetallics with sizes less than 800 nm were seen at the surface of detached interfaces. The grain size of copper rod near the interface is lower that of the center.
Keywords:
Authors
A.M. SHAHAB
School of Metallurgy and Materials Engineering, University College of Engineering, University of Tehran, Tehran, Iran, P.O. Box. ۱۵۵-۴۵۶۳.
S. A. A. AKBARIMOUSAVI
School of Metallurgy and Materials Engineering, University College of Engineering, University of Tehran, Tehran, Iran, P.O. Box. ۱۱۱۵۵-۴۵۶۳.