The Comparison of Martensitic Transformation Sequences Between Aged Ti-50.6 and Ti-51.0 at.% Ni Alloys by in-situ SEM Observations
Publish Year: 1396
نوع سند: مقاله ژورنالی
زبان: English
View: 367
This Paper With 8 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JEFM-1-1_003
تاریخ نمایه سازی: 25 تیر 1398
Abstract:
The comparison of martensitic transformation sequences between aged Ti-50.6 and Ti-51.0 at.%Ni alloys have been investigated by differential scanning calorimetry (DSC) and in-situ scanning electron microscopy (SEM). Ti-50.6 and 51.0 at.% Ni alloys were selected for evaluation of Ni concentrations. These alloys were heat-treated at 1223 K for 3.6 ks and then aged at 773 K for 3.6 ks. Although the Ti-50.6 and 51 at. % Ni alloys revealed the triple stage transformations during cooling, but the results of in-situ SEM observations showed that the sequence of these transformations was completely different from each other. Although, the distribution and size of Ti3Ni4 precipitates observed in various compositions were different from each other, but the heterogeneity in distribution and size of precipitates was a common feature of them. For both of the compositions, martensitic transformation sequences are quantitatively proved by comparing DSC measurements and SEM observations. The calculations show good agreement between DSC cooling curve and SEM observation results.
Keywords:
Authors
B. Karbakhsh Ravari
Department of Applied Science for Electronics and Materials, Interdisciplinary Graduate School of Engineering Sciences, Kyushu University, Kasuga, Fukuoka, Japan.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :