The Effect of Al Additive and Arc Melting Time on Synthesis of Ti۳SiC۲ MAX Phase using Ti/SiC/Al/Graphite
Publish place: Mechanics of Advanced Composite Structures، Vol: 9، Issue: 2
Publish Year: 1401
نوع سند: مقاله ژورنالی
زبان: English
View: 88
This Paper With 10 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-9-2_014
تاریخ نمایه سازی: 9 اردیبهشت 1402
Abstract:
In this study, the effect of different molar ratios of primary powders and arc melting setting time on the synthesis of Ti۳SiC۲ powder has been investigated. For this purpose, Silicon Carbide (SiC), Titanium (Ti), graphite (C) and aluminum (Al) powders with molar ratios of ۳Ti:۱.۲SiC:۰.۸C, ۳Ti:۱.۲SiC: ۰.۸C:۰.۱Al and ۳Ti:۱.۲CiC:۰.۸C:۰.۳Al were mixed by a planetary mill under an argon atmosphere for ۵h. The resulting mixture was formed with a press and subjected to arc melting at ۱, ۳, ۵, and ۱۰s. In samples containing Al additive, the purity of Ti۳SiC۲ increases with increasing arc melting setting time up to ۵s, and the purity decreases with increasing the arc time. The best result was obtained in the sample ۳Ti:۱.۲SiC:۰.۸C:۰.۱Al containing ۸۳.۶ wt% of Ti۳SiC۲, which was obtained during the ۵s arc melting.
Keywords:
Authors
Alireza Moradkhani
Faculty of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, Iran
Behnam Kozekanan
Department of Mechanical Engineering, University of Tabriz, Tabriz, Iran
Hamidreza Baharvandi
Department of Materials Engineering, University of Tehran, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :