Influence of Li addition on the microstructure and tensile properties of extruded Al-25 wt.%Mg2Si composite
Publish Year: 1392
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,168
This Paper With 5 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES07_302
تاریخ نمایه سازی: 28 آذر 1392
Abstract:
In this work, the effect of Li addition and hot-extrusion on the microstructure and tensile properties of Al-25 wt. %Mg2Si in-situ composite have been studied. Cast, modified and homogenized small ingots were extruded at520 °C at extrusion ratio of 6:1 and ram speed of 1mm/s. different techniques such as metallography and scanning electron microscope (SEM) were used to characterize the mechanical behavior, microstructural observations andfracture surface of this composite. With the addition of Li up to 0.5%, the average size of primary Mg2Si decreases from 186 μm to 15 μm in hot-extruded condition. Also, adding up to 0.5% of Li increases ultimate tensile strenght (UTS) and tensile elongation values. The highest UTS and elongation values were found to be 177 MPa and 8% respectively. Fracture surface examinations indicated a transition from brittle fracture mode in as-cast composite to ductile fracture in modified and extruded specimens
Keywords:
Authors
Asiyeh Montajabnia
Department of Materials Engineering, Science and Research branch, Islamic Azad University, Tehran, Iran
Ali Nemati
Department of Materials Engineering, Science and Research branch, Islamic Azad University, Tehran, Iran
Massoud Emamy
School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran