Preparation and investigation of polylactic acid, calcium carbonate and polyvinylalcohol nanofibrous scaffolds for osteogenic differentiation of mesenchymal stem cells
Publish place: Nanomedicine Journal، Vol: 3، Issue: 2
Publish Year: 1395
نوع سند: مقاله ژورنالی
زبان: English
View: 230
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_NAMJ-3-2_003
تاریخ نمایه سازی: 18 تیر 1398
Abstract:
Objective(s): In this study, the effect of electrospun fiber orientation on proliferation and differentiation of mesenchymal stem cells (MSCs) was evaluated. Materials and Methods: Aligned and random nanocomposite nanofibrous scaffolds were electrospun from polylactic acid (PLA), poly (vinyl alcohol) (PVA) and calcium carbonate nanoparticles (nCaP). The surface morphology of prepared nanofibrous scaffolds with and without cell was examined using scanning electron microscopy. Mechanical properties of electrospun nanofibrous scaffolds were determined with a universal testing machine. The in vitro properties of fabricated scaffolds was also investigated by the MTT assay and alkaline phosphatase activity (ALP).Results: The average fiber diameter for aligned and random nanofibers were 82 ± 12 nm and 124 ± 25 nm, respectively. The mechanical testing indicated the higher tensile strength and elastic modulus of aligned nanofibers. MTT and ALP results showed that alignment of nanofiber increased the osteogenic differentiation of stem cells.Conclusion: Aligned nanofibrous nanocomposite scaffolds of PLA/nCaP/PVA could be an excellent substrate for MSCs and represents a potential bone-filling material.
Keywords:
Authors
A. Doustgani
Department of chemical engineering, University of Zanjan, Zanjan, Iran
M. S. Pedram
Faculty of Veterinary Medicine, University of Tehran, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :