Investigation on Composition and Microstructural Morphology of the Fe-B-C Hardfacing Layers
Publish Year: 1398
Type: Journal paper
Language: English
View: 658
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- I'm the author of the paper
Export:
Document National Code:
JR_JEFM-3-1_001
Index date: 16 July 2019
Investigation on Composition and Microstructural Morphology of the Fe-B-C Hardfacing Layers abstract
The application of hardfacing materials for producing wear-resistant coatings on components working in wear conditions is one of the important advices in environmental protection and increasing the service life of engineering equipment. In this study, the microstructure of the hardfaced layers made by two cored wires containing Fe-B and Fe-B-C powder-based were investigated. ST37 plain carbon steel was used as the substrate and the deposition of the hardfaced layers was conducted by the flux cored arc welding (FCAW) process under single-, two-, and three-pass conditions. The microstructural and phase analyses were carried out by field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD), respectively. The results showed that the characteristic microstructures of the Fe-B hardfacing alloy layers comprised a matrix containing elliptical dendritic ferrite and the eutectic of (α-Fe2B). But, the Fe-B-C hardfacing alloy layers included columnar-like Fe2B, skeletal-like Fe2B, daisy like Fe3(C, B) and the eutectic of (P-Fe2B).
Investigation on Composition and Microstructural Morphology of the Fe-B-C Hardfacing Layers Keywords:
Investigation on Composition and Microstructural Morphology of the Fe-B-C Hardfacing Layers authors
M. R. Tavakoli Shoushtari
Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :