The Effect of Clay on the Ablation Behavior of NBR/OMMT Nanocomposites
Publish Year: 1390
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,312
متن کامل این Paper منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل Paper (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PPSRC2011_337
تاریخ نمایه سازی: 30 بهمن 1390
Abstract:
In special applications, elastomeric composite heat insulators are more attractive issues in compare to their similar non-elastomeric counterparts due to their excellent thermal stresses and large deformation bearing. A few works have been recently reported concerning ablative properties of elastomeric nanocomposites containing different fillers such as organically modified montmorillonite (OMMT). However, the effect of loading level of OMMT on the ablation behavior of elastomeric heat insulator has not been reported.In this work, the ablative properties of nitrile butadiene rubber nanocomposite with difference loading levels of OMMT were investigated. The back temperature of elastomeric nanocomposite heat shield with different thickness (2.5 and 5 mm) was measured using oxyacetylene flame test and the effect of clay on it was studied. Also, the ablation rates were calculated.The results showed that NBR/OMMT nanocomposite with higher loading level of clay (13.35 wt%) has lower ablation rates (about 7 times in mass loss and about 11 times in erosion rate) and lower magnitude of back temperature (about 513°C) than its composite counterpart. From the viewpoint of thermal shielding capability, elastomeric nanocomposites exhibit better ablation resistance.
Keywords:
Authors
Fatemeh Arabgol
Polymer Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University, P.O. Box: ۱۴۱۱۵-۱۱۴, Tehran, Islamic Republic of Iran
Mehrdad Kokabi
Polymer Engineering Department, Faculty of Chemical Engineering, Tarbiat Modares University, P.O. Box: ۱۴۱۱۵-۱۱۴, Tehran, Islamic Republic of Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :