Optimization of Nano-crystalline Gamma Al2O3 Powders Preparation Using Taguchi L-4 Method
Publish place: 12th National Iranian Chemical Engineering Congress
Publish Year: 1387
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,667
This Paper With 12 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NICEC12_700
تاریخ نمایه سازی: 30 شهریور 1387
Abstract:
Nano-structured gamma Al2O3 powders were prepared by combustion synthesis method utilizing serine as complexing agent. The product was sonicated to obtain nano powders. A Taguchi L-4 statistical design of combustion synthesis utilized to optimize the production of gamma-alumina powder. The product was characterized by XRD, BET, SEM, and LLS. Nano crystalline γ-alumina with crystal size between 4.26nm to 5.47nm and α-alumina powders with crystal size 24.51nm and 28.62nm were obtained by combustion synthesis. The specific surface area was measured by BET method. Result shows 75.21m2/g. The average particle size after sonication of product, observed by LLS, was 79.32 nm.
Keywords:
Authors
Mohammad Edrissi
Chemical Engineering Department, Amirkabir University of Technolog
Reza Norouzbeigi
Chemical Engineering Department, Amirkabir University of Technology
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :