EFFECT OF AGING STEP ON THE TEXTURE OF SBA-15 PREPARED AT SHORT RIPENING TIME
Publish Year: 1393
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,158
This Paper With 7 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
TCPCO01_252
تاریخ نمایه سازی: 27 فروردین 1393
Abstract:
In this paper, the influence of aging (hydrothermal) time and temperature on the characteristics of SBA-15 mesoporous silica materials. The results indicated SBA-15 sample obtained at short-time ripening of 4 hour (hr) contained more silanol groups that two-dimensional (2-D) hexagonal SBA-15 mesoporous structure than the conventional SBA-15 material (24 hr). As well, the sample synthesized after 4 hr of ripening at 40°C followed by 24 hr of hydrothermal operation at 100ºC, demonstrated enhancement of 2-D hexagonal order compared to other samples. The synthesized material was characterized using small angle XRD, SEM, TEM and BET techniques
Keywords:
Authors
m Sadeghi
Department of Oil, Gas and Petrochemical Engineering, Persian Gulf University, Boushehr, Iran.
a izadbakhsh
Department of Oil, Gas and Petrochemical Engineering, Persian Gulf University, Boushehr, Iran.
kh niknam
Department of Chemistry, Faculty of Sciences, Persian Gulf University, Bushehr
s.a Sajjadi
Department of Oil, Gas and Petrochemical Engineering, Persian Gulf University, Boushehr, Iran.
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :