Synthesis and characterization of HA-YSZ
Publish place: The 14th Conference of chemical Engineering
Publish Year: 1391
نوع سند: مقاله کنفرانسی
زبان: English
View: 1,242
This Paper With 6 Page And PDF Format Ready To Download
- Certificate
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NICEC14_561
تاریخ نمایه سازی: 3 آذر 1391
Abstract:
HA-Y2O3-ZrO2, a nano-composite as a biomaterial, was successfully synthesized via Sol-gel method. . The study of the crystal structure through the X-ray Diffraction (XRD) confirmed the formation of tetragonal zirconia (t-ZrO2) and hydroxyapatite (HA). The study of the chemical state by the X-ray photo-emission spectroscopy (XPS) and the Fourier transform infrared spectroscopy (FT-IR) confirmed the HA-Zirconium bond in the ternary composite system.The study of the biomaterial thermal behaviour by simultaneous thermal analysis (STA) verified that the presence of the HA beside the Zirconium , reduces the tetragonal formation temperature from 1100°C to be 400°C. Transmission Electron Microscopy (TEM) of the sample represented the average particle size as around 20 nm for t-ZrO2 and 50 nm for HA; moreover, it illustrated the fine dispersion of the t zrO2in the HA matrix
Keywords:
Authors
Sahar Salehi
Department of material engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
Ghadir Rajabzadeh
Nanotechnology Department, Research Institute of Food Science and Technology, Mashhad, Iran
Ali Nemati
Department of material engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
مراجع و منابع این Paper:
لیست زیر مراجع و منابع استفاده شده در این Paper را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود Paper لینک شده اند :