The Influence of Graphene Oxide on Mechanical Properties andDurability Increase of Concrete Pavement

Herein, the performance of graphene oxide (GO) in improving mechanical properties and subsequently reducing the permeability of cement composites used in concrete pavement, is studied. A polycarboxylate superplasticizer wasused to improve the dispersion of GO flakes in the cement. The mechanical strength of graphene-cement nanocomposites containing 0.1–2 wt% GO and 0.5 wt% superplasticizer was measured and compared with that of cement prepared without GO. We found that the tensile strength of the cement mortar increased with GO content, reaching 1.5%, a 48% increase in tensile strength. Ultra high-resolution field emission scanning electron microscopy (FE-SEM) used to observe the fracture surface of samples containing 1.5 wt% GO indicated that the nano GO flakes were well dispersed in the matrix, and no aggregates were observed. FE-SEM observation also revealed good bonding between the GO surfaces and the surrounding cement matrix. In addition, XRD diffraction data showed growth of the calcium silicate hydrates (C-S-H) gels in GO cement mortar compared with the normal cement mortar. Growths of the calcium silicate hydrates (C-S-H) gels causes reduce in permeability and consequently improvement in durability of the cement composite.

The Influence of Graphene Oxide on Mechanical Properties andDurability Increase of Concrete Pavement Keywords:

Cement , nanocomposite , graphene oxide , mechanical properties , tensile strength. Pavement